ABS
Extrusion Grade
ISOPAK®569P
| Item Name | ISOPAK®569P |
|---|---|
| Main Application | Good for Thermo-Forming, Suitcase industry, Tube, Plate, Safety helmet |
| Package | 25 kg |
| PROPERTIES | Test Method | Test Condition | Unit | Value |
|---|---|---|---|---|
| IZOD Impact Strength (Notched) |
D256 Method A |
23℃ 1/8¨x1/2¨x5/2¨ |
kg-cm/cm | 50 |
| Melt Flow Index | D1238 | 220℃, 10kg/cm2 200℃, 5kg/cm2 |
g/10mins g/10mins | 5 0.5 |
| Tensile Strength | D638 | 23℃, 1/8¨ 5.0mm/min |
kg/cm2 MPa |
425 33 |
| Flexural Strength | D790 | 23℃ 2.8mm/min |
kg/cm2 Mpa |
600 59 |
| Heat Distortion Temp. | D648 | 18.56kg/cm2 1/2¨x1/2¨x5¨ Unannealed |
℃ | 87 |
| Rockwell Hardness | D785 | 23℃ | R Scale | 103 |
| Specific Gravity | D792 | 23℃ | 1.03 | |
| Flammability | UL-94 | 1/16¨ sample | HB |
ISOPAK®569E
| Item Name | ISOPAK®569E |
|---|---|
| Main Application | Suitcase industry, Tube, Plate, Safety helmet |
| Package | 25 kg |
| PROPERTIES | Test Method | Test Condition | Unit | Value |
|---|---|---|---|---|
| IZOD Impact Strength (Notched) |
D256 Method A |
23℃ 1/8¡ x1/2¡ x5/2¡ |
kg-cm/cm | 38 |
| Melt Flow Index | D1238 | 220℃, 10kg/cm2 | g/10mins | 9.0¡1.0 |
| Tensile Strength at Yield at Break |
D638 | 23℃, 1/8¡ 5.0mm/min |
kg/cm2 | 410 360 |
| Flexural Yield | D790 | 23℃ 2.8mm/min |
kg/cm2 | 600 |
| Heat Distortion Temp. | D648 | 18.56kg/cm2 1/2¡ x1/2¡ x5¡ Unannealed |
℃ | 86 |
| Rockwell Hardness | D785 | 23℃ | R Scale | 102 |
| Specific Gravity | D792 | 23℃ | 1.03 | |
| Flammability | UL-94 | 1/16¡ sample | HB |